Custom M-ATPU Foam Sheet Suppliers, OEM/ODM Factory - Suzhou Shincell New Material Co., Ltd.

M-ATPU Foam Sheet

M-ATPU is microcellular aliphatic TPU foam, produced using TPU as the substrate with clean supercritical carbon dioxide as blowing agent to form a large number of microcells in the matrix.

Component

Thermoplastic Aliphatic Elastomer ATPU

Characteristic

Super light weight

Clean and environmental friendly

Outstanding resilience

Good cushion performance

Excellent low temperature resistance

Excellent yellowing resistance

Reusable

Basic Physical Properties

Test Item	Test Method	Unit	05	06	07	09	10
Density	ISO 845:2006	g/cm³	0.05±0.02	0.06±0.02	0.07±0.02	0.09±0.02	0.10±0.02
Hardness	SATRA TM 205-16	Shore C	24±4	27±4	30±4	37±4	40±4
Size	-	Length mm Width mm Thick mm	1600-1650 1200-1250 32	1550-1600 1150-1200 30	1450-1500 1100-1150 30	1400-1450 1050-1100 28-30	1350-1400 1000-1050 24-26
Colour fastness	GB250-1995 30 days of sunshine	-	4-5
Heat resistance	75℃-24h 85℃-24h	%	＜1 1~3
Appearance	-	-
SEM	-	-

Test results of mechanical properties

Test Item	Test Method	Unit	05	06	07	09	10
Compression Set	ASTM D395 50℃-6h-30min	%	≤54	≤51	≤47	≤33	≤30
Compression Set	ASTM D395 50℃-6h-24h	%	≤16	≤11	≤11	≤10	≤9
Compression Set	SC 25℃-6h-30min	%	≤54	≤50	≤46	≤16	≤11
Compression Set	SC 25℃-6h-24h	%	≤14	≤14	≤12	≤7	≤3
Tensile Strength	ISO 1798:2008	MPa	2.01	2.29	2.56	3.44	3.49
Elongation at Break	ISO 1798:2008	%	151.23	159.26	181.88	150.22	154.45
10% Compress Pressure	ASTM- D1621-2010	MPa	0.028	0.031	0.046	0.058	0.088
50% Compress Pressure	ASTM-D1621-2010	MPa	0.126	0.131	0.161	0.197	0.238
Method A Tear Trouser Test	ISO 8067:2008	N/cm	16.13	17.75	24.03	24.26	24.6
Method B Tear Angle Test	ISO 8067:2008	N/cm	38.80	40.25	46.62	52.16	53.43
Resilience	ASTM D3574	%	79.2	79.3	79.5	82.0	79.7

Shincell New Material CO.,LTD.

　　Shincell is a company dedicated to developing sustainable foaming technologies and manufacturing clean, environmentally friendly lightweight foam materials. And we also a China custom M-ATPU Foam Sheet supplier and OEM/ODM M-ATPU Foam Sheet factory. We use N2 and CO2 gases commonly found in the air to expand plastics and form a large number of micro and nano bubbles inside, a purely physical foaming process.
　　Shincell was founded by Dr. Xiulei Jiang. He started his research on supercritical fluid foaming technology at East China University of Science and Technology in 2003 and proposed the technical process of supercritical molded microcellular foaming. His early interest lies in lightweight and high-strength foam materials, and his main product is PP microcellular foam sheets. Inspired by the Adidas boost midsole derived from TPU beads foaming, he started to study the sheet foaming technology of TPU elastomer material in 2015. Based on these years of basic research, Shincell has formed two series of products: soft high-elasticity lightweight materials and hard high-strength lightweight materials.Soft high elasticity products include TPU, TPEE and PEBA, PEBAX, etc., and hard high strength products include PP, PVDF, PPO, PA, etc.

　　We focus on the research and development of foaming technology, we will continuously optimize the process, challenge our past self, improve efficiency and reduce cost, and continuously launch new products. Our foam materials are all thermoplastic and no chemical blowing agents are added in the foaming process, nor are they chemically cross-linked. We can provide our customers with online custom M-ATPU Foam Sheet products at preferential factory wholesale prices. And compared to traditional foaming materials, our foam materials are recyclable, non-toxic and environmentally friendly, and meet the needs of sustainable development!